Two-Dimensional High Spatial-Resolution Dosimeter Using Europium Doped Potassium Chloride
H Li1*, J Driewer2 , Z Han3 , D Low4 , D Yang1 , Z Xiao1 , (1) Washington University School of Medicine, St. Louis, MO, (2) University of Nebraska Medical Center, Omaha, NE, (3) Brigham and Womens Hospital and Harvard Medical School, Boston, MA, (4) UCLA, Los Angeles, CA
Presentations
TH-C-19A-12 Thursday 10:15AM - 12:15PM Room: 19APurpose: Recent research has shown that KCl:Eu2+ has great potential for use in megavoltage radiation therapy dosimetry because this material exhibits excellent storage performance and is reusable due to strong radiation hardness. This work reports our attempts to fabricate 2D KCl:Eu2+ storage phosphor films (SPFs) using both a physical vapor deposition (PVD) method and a tape casting method.
Methods: A thin layer of KCl:Eu2+ was deposited on a substrate of borosilicate glass (e.g., laboratory slides) with a PVD system. For tape casting, a homogenous suspension containing storage phosphor particles, liquid vehicle and polymer binder was formed and subsequently cast by doctor-blade onto a polyethylene terephthalate substrate to form a 150 μm thick SPF.
Results: X ray diffraction analysis showed that a 10 μm thick PVD sample was composed of highly crystalline KCl. No additional phases were observed, suggesting that the europium activator had completed been incorporated into the KCl matrix. Photostimulated luminescence and photoluminescence spectra suggested that F (Cl-) centers were the electron storage centers post x ray irradiation and that Eu2+ cations acted as luminescence centers in the photostimulation process. The 150 μm thick casted KCl:Eu2+ SPF showed sub-millimeter spatial resolution. Monte Carlo simulations further demonstrated that the admixture of 20% KCl:Eu2+ and 80% low Z polymer binder exhibited almost no energy dependence in a 6 MV beam. KCl:Eu2+ pellet samples showed a large dynamic range from 0.01 cGy to 60 Gy dose-to-water, and saturated at approximately 500 Gy as a result of its intrinsic high radiation hardness.
Conclusions: This discovery research provides strong evidence that KCl:Eu2+ based SPF with associated readout apparatus could result in a novel electronic film system that has all the desirable features associated with classic radiographic film and, importantly, water equivalence and the capability of permanent identification of each detector.
Funding Support, Disclosures, and Conflict of Interest: This work was supported in part by NIH Grant No. R01CA148853. The authors would like to thank Paul Leblans (AGFA Healthcare, Belgium) for many helpful discussions on this topic.